Shape memory alloy (SMA) helical springs are special mechanical parts that require a previous evaluation of its behavior for application. Therefore, in this paper thermal and mechanical behaviour of superelastic Ni-Ti SMA helical extension springs manufactured by investment casting (IC) are evaluated. Phase transformation temperatures were measured by Electrical Resistance as a function of Temperature (ERT) and Differential Scanning Calorimetry (DSC). Tensile tests were carried out within strain and temperatures ranges. The pitch angle and stiffness of each spring were determined. Results demonstrated that Ni-Ti SMA helical springs produced by IC presented phase transformation corresponding to the superelastic effect (SE). The reversible deformations under tensile test were of the order of 70%. The mechanical behavior as function of temperature revealed a linear relationship between maximum force and spring temperature.

This paper presents a thermal and microstructural characterization of Cu87-xAl13Nbx (wt%) high temperature shape memory alloys (HTSMA), with Nb contents ranging from 1 to 3%. The alloys were obtained by arc melting under argon atmosphere. Thermal characterization was performed by differential scanning calorimetry (DSC), revealing that the phase martensitic transformation of all the studied alloys occurs in the range of 200 ºC to 450 ºC. Thermal cycling in this temperature range caused the martensitic transformation to disappear after approximately 6 cycles. However, a new heat treatment at 850 ºC followed by water quenching causes the martensitic transformation to be recovered. Microstructural characterization was performed using optical microscopy (OM) and scanning electron microscopy (SEM), revealing the presence of Nb precipitates in a Cu-Al martensitic matrix, mainly in the Nb-rich compositions. These different microstructures with Nb particles cause a hardness variation that initially decreases between 0.5 %Nb (275HV) and 1.0 %Nb (225HV), then increasing continuously up to 3.0% Nb (380HV).